SEALXPERT WRAP SEAL ULTRA QUICK REPAIR KIT - WSU0212
| Previous | 75 / 75 | Next |
Description :
FEATURES:
CURING TIME:
OPERATING PRESSURE:
FEATURES:
- Repairs under active leak up to 150 psi (11 kg/cm2) pressure
- No shutdown required
- Works on any metal or non-metal pipes
- Applicable to pipes up to 18' (457 mm) diameter
- Repairs leak in 15 minutes
- Withstand pressure up to 500 psi (35 kg/cm2)
- Withstand temperature up to 200 °C (392 °F)
- Safe for drinking water and resistant to most chemicals
- Ideal for pipeline reinforcement
- Steel
- Copper
- Aluminium
- Galvanized steel
- PVC
- CPVC
- Stainless steel
- Polyethylene
- Polypropylene
- Cast-iron
- Concrete
- FRP/GRE
- Oil
- Water (drinking water, wastewater, steam)
- Solvents (acetone, toluene, MEK, ethyl alcohol)
- Mild acids (hydrochloric acid, sulfuric acid) and alkalis
- Chemical (ethylene glycol, xylenes, ammonia)
- Hydrocarbons
- Bases
- Slurries
- Fuels (petroleum, diesels, gasoline)
- Gases (LNG, LPG)
- Organic salts
- 1 minute at 30 °C (86 °F)
CURING TIME:
- 30 minutes at 30 °C (86 °F)
- Heat may be applied to decrease curing time
- Unopened foil pouch may be immerse in cold water prior to repair to add working and curing time.
- Pipe repairs
- active pipe leaks
- sealing joints
- hazardous material spill control
- reinforce thinning walls
- Repairs in hard to reach areas
- Underwater repairs
- -50 °C (-58 °F) to 200 °C (392 °F)
OPERATING PRESSURE:
- Recommended for pressure up to 500 psi (35 kg/cm2)
- (Result vary depending on pipe size, type of pipe, hole size, pipe content and method of application)
| Tensile strength | : | 3920 psi (276 kg/cm2) |
| Bond strength | : | 230 psi (16 kg/cm2) |
| Tensile elongation | : | 1.2 % ± 0.7 % |
| Compression strength | : | 13750 ± 530 psi (967 ± 37 kg/cm2) |
| Yield strength | : | 2260 psi (159 kg/cm2) |
| Cured hardness | : | 82 Shore D |
| Dielectric strength | : | 400 Volts/mil |